牌号简介 About |
---|
Ebarta AH 140是一种非常薄的液体双组分环氧树脂,具有高强度和高耐热性。由于它具有很好的浸渍和润湿性能,适用于玻璃纤维或碳纤维织物的高强度部件的层压树脂。特别是对于薄层压板而言,在室温下固化后,在80°C下16小时的后固化对于确保完全固化至关重要。否则,非后固化层压板将变脆,且层间的粘合力不足。应用手工层压真空输注碳纤维观光层压板汽车工业用造船层压板航空性能用非填充超薄液体长加工时间高耐热性高强度优异的湿出特性 ebalta AH 140 is a very thin liquid two-component-epoxy resin with high values of strength and high heat resistance. Due to its very good impregnating and wetting properties it is suitable as laminating resin for high-strength components with fabrics of glass -or carbon fiber. Especially for thin laminates, a post-curing of 16 hours at 80°C, after curing at room temperature, is essential in order to guarantee a complete curing. Otherwise the non post-cured laminate will be brittle and the adhesion of the layers with each other will not be sufficient. Applications Hand laminating Vacuum infusion carbon fibre sight laminates Laminates for boatbuilding Laminates for automotive industry Laminates for aeronautic Properties unfilled very thin liquid long processing time high heat resistance high strength excellent wet-out characteristics |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
30 到 46 | kJ/m² | ISO 179 |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
20℃ 20℃ |
1.10 到 1.14 | g/cm³ | |
粘度 viscosity |
|||
25℃ 25℃ |
0.35 到 0.50 | Pa·s | |
固化时间 Curing time |
|||
20℃ 20℃ |
48 到 72 | hr | |
储存稳定性 storage stability 2 |
|||
20 ℃ 20 ℃ 2 |
90 到 110 | min | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 7619 | ||
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
玻璃化转变温度 Glass transition temperature |
℃ | TMA | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
后固化时间 Post curing time |
|||
60℃ 60℃ |
hr | ||
80℃ 80℃ |
hr | ||
120℃ 120℃ |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 200 g |
【新闻资讯】查看全部
2016美学塑料创新运用国际研讨会于上海盛大开幕
2016-06-24 2016美学塑料创新应用国际研讨会,于6月24日在上海盛大开幕。研讨会开始时,主办方塑可丽®特邀媒体对参会的三位嘉宾进行深度采访。 设计是市场占中至关重要的一环。好的产品设计能迅速抓住用户需求,占领市场。美学塑料带来的靓丽外观大大增加了设计感。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |